Matter
- Name
- Anorthositic glass (20-50µm grains)
- Family
- solid
- Database
- Experimentalists
- Parent matter
- Anorthositic glass
- Origins
- laboratory
- Provider
- Volcanologist Laboratory at RomaTre University
- Preparation
- selected components
- Phase type
- solid
- Shape
- compact
- Texture
- loose granular
- Type of porosity
- particulate
- Density
- 2.704 $\pm$ 0.001 $g.cm^{-3}$
- Grain density
- 2.704 $\pm$ 0.001 $g.cm^{-3}$
- Grain sizes
-
Grains Size min Size max Size median Size width Size mass fraction Grain shape #1 20.0 ${\mu}m$ 50.0 ${\mu}m$ 1.0 amorphous - Size method
- sieving between 2 sieves
- Oxides
-
Formula $SiO_{2}$ $TiO_{2}$ $Al_{2}O_{3}$ $Fe_{2}O_{3}$ $MnO$ $MgO$ $CaO$ $Na_{2}O$ $K_{2}O$ $P_{2}O_{5}$ Mass fraction (%) 48.18 0.08 29.36 1.78 0.03 1.92 15.85 2.24 0.08 0.01 - Oxides comments
- Fe2O3 is total iron amount; L.O.I. 0.23%
- Title
- preparation of powder of anorthositic glass
- Matters
- Matter
- Anorthositic glass (20-50µm grains) (this matter)
- Processing steps
-
Step Date Type Process Changes #1 2010-06-01 mechanical Anorthositic glass has been crushed to grain sizes lower than 1 mm glass in powder with sub-mm grains #2 2010-06-01 mechanical Anorthositic glass grains have been quartered and crushed to powder glass in powder #3 2010-06-01 mechanical Glass powder has been sieved between 50 and 20 µm sieves Glass powder with grain size range between 20 and 50 µm - Comments
- sieved glass samples with various grain sizes were produced at IAPS laboratory)