- Database
- Experimentalists
- Date
- 1997-01-01
- Surface roughness
- polished
- Substrate material
- epoxide resin (epofix)
- Substrate comments
- sample rear side embedded in resin (25mm diam.) for handling during polishing and measurement
- Comments
- original pellet diameter was 13mm, pellet mass 0.06g, volume loss 50-80% during pyrolysis
- Temperature
- 300.0 $\pm$ 5.0 $K$
- Temperature max
- 1073.0 $\pm$ 5.0 $K$
- Time at Tmax
- 120.0 $min$
- Type
- ambient air
- Fluid temperature
- 300.0 $\pm$ 5.0 $K$
- Fluid pressure
- 1.0 $bar$
- Number
- 1
- Layers
- Title
- Pyrolysis of cellulose pellets
- Matters
- Sample
- Embedded/polished cellulose pellet pyrolyzed at 800°C (this sample)
- Processing steps
-
Step Chronology Date Type Process Changes #1 during layer formation pressure 0.06g of cellulose powder are pressed in a pressing tool of 13mm diameter under 2 tons load #2 after layer formation pressure pellets were outgassed in vacuum (pressure 0.01 mbar) for 3 hours #3 after layer formation thermal pellets were heated (180K/h) to 800°C under Ar atmosphere, kept for 2 hours at reaction temperature, cool-down at 180K/h release of volatile elements and groups #4 after layer formation mechanical pellet rear side was embedded in epoxy resin (25mm diam.), after that the front side was polished